Re: [MW:33858] Stabilizing treatment of SS plate /components

Mainly avoids WELD DECAY.

Thanks & Regards

J.Gerald Jayakumar

On Monday, 26 December, 2022 at 10:21:46 am IST, 'james gerald' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Just to add, the purpose of this HT is to form stable TiC & NbC and hence the name stabilization HT

Thanks & Regards

J.Gerald Jayakumar

On Monday, 26 December, 2022 at 09:28:49 am IST, 'james gerald' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Basically it is performed to form TiC and/ NbC and so no further C available for IGC attack/

Thanks & Regards

J.Gerald Jayakumar

On Monday, 26 December, 2022 at 08:48:47 am IST, 'Sankaran Sp' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Dear  Mr.Prakash,

stabilized heat treament is required for stablized staniless steel only, not for all SS grades.

stabilizing alloys of Like : Nb/Cb, Ti ,Zr & others are speciafiaclly added in the normal SS aloys to avoid senstitization, after solution heat treatement we don't know about whether these stabilzed alloys are setteld in grain boundry or in the core. hence to ensure the stabilized alloys in grain boundry this stabilized heat treatment is essential, as per ASTM A 182 ot ASTM A 351 this stabilized heat teratment is given as subimentary variable for forging & casting respectively. During stabilized heat treatement soaking hour to given as 4 hour (min).          

 

Regards,

Sankaran.SP

Welding & Metallurgy expert

Coimbatore, India. 

On Thursday, 22 December, 2022 at 08:53:38 am IST, 'Prakash Hegde' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Hi! Friends

Why some of the client spec ask for

Stabilizing treatment (At lower temperature than solution annealing i.e. about 900C) of already solution annealed plate but not Welded SS components

Especially  304H,347,321

Regards

Hegde

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/743927190.1795927.1671599012641%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/709916209.2786676.1671884370625%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/517515973.2327354.1672026846327%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/1076274235.932856.1672029576777%40mail.yahoo.com.