Re: [MW:31898] How to read pressure vessel fabrication 2D drawings

By Materials & Welding
In all the years that I have of experience (and I have been in ASME Audits) I have never seen that ASME Y14.5 is used for the engineering of Pressure Vessels, I suggest you see a tutorial on the internet, help you a friend who has more experience on the subject and in short: you have to be familiar with ASME BPVC Section VIII Div. 1, otherwise it will be very difficult for you to understand Pressure Vessels and their engineering.
Greetings and happy new year.

El sáb, 2 ene 2021 a las 2:57, Jamie Reyes (<jamiejrmachineco@gmail.com>) escribió:
Hello,
Not for sure how well versed you are with standards, but here you go.
ASME Y14.5 Standard, latest addition, would be a good starting point. www.asme.org
Happy reading, cheers!

The following are ASME Y14 Standards that are basic engineering drawing standards:

ASME Y14.1, Decimal Inch Drawing Sheet Size and Format 

ASME Y14.1M, Metric Drawing Sheet Size and Format 

ASME Y14.2, Line Conventions and Lettering

ASME Y14.3, Orthographic and Pictorial Views

ASME Y14.5, Dimensioning and Tolerancing

ASME Y14.24, Types and Applications of Engineering Drawings

ASME Y14.34, Associated Lists

ASME Y14.35, Revision of Engineering Drawings and Associated Documents

ASME Y14.36, Surface Texture Symbols

ASME Y14.38, Abbreviations and Acronyms for Use on Drawings and Related Documents

ASME Y14.41, Digital Product Definition Data Practices

ASME Y14.100, Engineering Drawing Practices



On Fri, Jan 1, 2021 at 11:19 PM Shahil Saini <sainishahil98@gmail.com> wrote:
Hello everyone, Happy New year to all of you,

I am a fresher in pressure vessel  fabrication field, can anyone help me to get the nice place from where I learn to read pressure vessel fabrication 2D drawings.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALfBO_9DW52Y030Q1q6%3Da%2BAdD_uK-N2N9%2BebtSfNk-nk_eyCpA%40mail.gmail.com.
--
Regards,
Jamie Reyes
J.R. Machine Company, Inc.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJNUtUNzqcvS2Ewprquv-5c3sxv_fgL7RTn-tXmaRxNAsHUM3Q%40mail.gmail.com.


--

Ing. José Juan Jiménez Alejandro

Independent Consultant in Parts

and Pressure Equipment

SUMMIT MÉXICO - TPI

https://www.linkedin.com/in/summit-m%C3%A9xico-tpi-760047137/

Móvil +52 1 812 352 4606

Skype: jjjimeneza





--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAO5ZurJgm0ucqr%2BoLUH%3DUdawXuoy4P4pGBn-zzsmtkSnsFOCNg%40mail.gmail.com.

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more