Re: [MW:31898] Continuous crack in forged duplex ring by PAW process

By Materials & Welding
HI,

ER 2594 has both Austenitic & Ferritc  Str.   Better to do with ER 309 L Or ER 312 L 
Also Make sure Grind off all the fatigue Layer completely . Deposit with low heat Input .also slow cooling ( cover by glass wool / welding blanket)

Kr
Das

On Sat, 2 Jan 2021 at 17:41, SURESH <qms.pjgpl@gmail.com> wrote:
Dear Experts
Need all your experience sharing on the below problem.

Material: ASTM A182, F55
Process: PAW
Welding: Hard facing weld overlay
Consumable ERCoCr-B (Stellite 12)
Layer deposited: 2 Layers
Deposition thick: 3 to 4mm ERCoCr-B on Base material
Interpass maintained: 150*C

During weld deposition of PAW process on 2nd layer itself crack has been propagated. We tried to rework by grinding and touch up, from that moment crack has been developed. If we tried to attend the crack place, other place are developing crack. Also now we again tried to rework, crack has been developing all the place, kindly tell me where this goes wrong?????

We are confused to do rework. As we goes deep to remove the crack, so we tried to grind 4mm deep now again deposited ER2594 by Tig process and then we follwed to weld by ERCoCr-B filler by TIG process. Again crack is developing enormously.

Please give valuable input to overcome from where we goes wrong in this?


REGARDS
SURESH 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/7aa85aac-7d40-4817-8c7e-4277f7865b76n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJyLdkpGu6AVdu8H6WVsyBFWMeQZswgKtEBDkTG56thmwnvRUw%40mail.gmail.com.

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more