[MW:21441] SS welding quenched by water

Dear all,

316L welding joints(6joints) were hot  welding condition quenched by cold water (20C) due to leakage...on upper side pipe.

Is there is metallurgy effect on SS welding due to this sudden quanching??

Regards
Mohd.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

[MW:35693] egwuanimkwujacobisrael@gmail.com

Dear all, No. MPI can only detect defect that is 1 to 2 mm dept. Therefore the paint must have mask the defect. Thanks. Egwuanimkw...