10 % RT is no where mentioned in the CODE it says only Full and Spot,
if the repair is found in RT then 2 spots should be taken,one at A side and other at B side ( considering spot is A-B) if again repair is found in one of the film, then 2 more shots shall be taken at each end. f again repair is found then you have to cut full joint and reweld.
and generally if crack is found then its a serious issue and customer will ask for more shots
pankaj
On Fri, Oct 21, 2011 at 9:49 PM, Vimal Kumar <vimal.fajar@gmail.com> wrote:
Hi all,
Can you pls help me, we have given order to our vendor in china for making ASME Pressure vessel, they have done 10% RT shot in long seam welding, but they have found crack and they rectify and again and then taken RT is passed and they delivered the item to singapore, but our client has raised concern that we need to RT in two more shot, but it was missing
Is it mention any where in the ASME about the two additional shot?
Which spec say that 10% RT on long seam?
Client never mentioned anything about this requirement, we strictly follow ASME
With regards
Vimal Kumar
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment