Hi Israr,
Regarding the heat treatment for lined vessel you can refer ASME SEC. VIII Div. 1 section UCL 34 and for examination of stainless lining refer UCL 36.
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Ali Asghari
Sent: December 30, 2008 1:54 PM
To: materials-welding@googlegroups.com
Subject: [MW:1430] Re: PWHT Requirement for clad plate vessel
Hi
please reply these question.
how much the thickness of lining?
what is the material of shell?
From: israr <ahmedisrar.nm@gmail.com>
To: Materials & Welding <materials-welding@googlegroups.com>
Sent: Thursday, December 25, 2008 1:44:00 PM
Subject: [MW:1422] PWHT Requirement for clad plate vessel
Dear Friend,
i have a vessel of 70 mm thick with internal lining of ss 316L plate.
I am not getting how to carryout heat treatment after welding of
internal lining,
I have suggested to use clad plate but there may chances to open clad
during heat treatment.
please help.
Regards
Israr Ahmed
Sr. Engineer QA/QC
This e-mail, including any attached files, may contain confidential and privileged information for the sole use of the intended recipient. Any review, use, distribution, or disclosure by others is strictly prohibited. If you are not the intended recipient (or authorized to receive information for the intended recipient), please contact the sender by reply e-mail and delete all copies of this message.
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
No comments:
Post a Comment