Re: [MW:33365] Clarification on Case hardening process

Material is not suitable for surface hardening as it is a ordinary construction steel.

Verstuurd vanaf mijn iPhone

Op 5 aug. 2022 om 08:07 heeft SURESH <qms.pjgpl@gmail.com> het volgende geschreven:

Dear Experts
Please need some suggestions on the below query.

Case Hardening process to achieve 60±2 HRC, Hardness Depth:1.5mm

Material: EN 10025-2 Grade S355J2/ 1.0577 DIN

We have tried carburizing and Nitriding methods to achieve this, but we have failed to achieve 60HRC. Instead, we achieved only 41HRC at the top surface and 23HRC on the 1.5mm surface during the examining in hardness survey.

Can anyone help me out with how to achieve this hardness?


Regards
S.Suresh

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/4ef679e3-7936-420a-893a-20bddf81843en%40googlegroups.com.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...