Re: Fw: [MW:30441] Re: Welding of S32750 super Duplex Steel

Dear Sir,

Thank you very much for your valued reply.

Same is applicable for SA 790 UNS S32750 to SA 240 Gr. 316L welding?

Please confirm.

On Thu, Jan 30, 2020 at 10:27 AM 'Amitabh Bhattacharya' via Materials & Welding <materials-welding@googlegroups.com> wrote:

Resending ..
The recomended GTAW filler alloy is SFA 5.9 ER2594 & not ER2507
Inconvenience is regretted.
Thanks Amitabh

----- Forwarded Message -----

From: Amitabh Bhattacharya <amitabh_3@yahoo.com>
To: "materials-welding@googlegroups.com" <materials-welding@googlegroups.com>
Sent: Tuesday, January 28, 2020, 09:36:56 AM EST
Subject: Re: [MW:30429] Re: Welding of S32750 super Duplex Steel

Hello
SA790 UNS S32750 is the specification for Super Duplex Pipes & Tubes .

Therfore use of ER2507 filler alloy will help in Ferrite-Austenite balance .

Weld metal producing PREN> 40 is requirement for Corrosion properties for such joints..

I would use the attached brochure for further studies & weld alloy selection.
Hope this helps
Amitabh

On Tuesday, January 28, 2020, 03:29:19 AM EST, Bien_ND / weldinginspections.net <bck055@gmail.com> wrote:

I recommend to select AWS A 5.9 ER2209 or ER309LMo.
Refer to API RP 582 Table A.3.

On Saturday, January 25, 2020 at 4:51:48 PM UTC+7, VIshaL wrote:
Dear Experts,

One of our project we have to weld material with GTAW process as per following.

1. SA 790 UNS S32750 to SA 780 UNS S32750

2. SA 790 UNS S32750 to SA 240 Gr. 316L

Request you to please confirm suitable filler wire Grade as well as any special care require during welding.

Thanks in advance.

VIshaL SUTHAR

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/11253781-f179-4a53-acbd-27309ea7a4d2%40googlegroups.com
.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/362492790.1048873.1580318276764%40mail.yahoo.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAOZ%2B%2BqB7_7cUz7K2fmTGzbNhXYyEnzLtUs_Nqo2cA9Vy02jmqQ%40mail.gmail.com.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog