Re: [MW:24802] RE: 24789] Regarding FCAW in SS

By Materials & Welding
In fact, SS with FCAW process provides excellent finish, even ripples,  100 % radio graphic welds
due to duel shielding, good fusion line, higher efficiency -- all compared to MIG or SMAW processes.

In a sense, MIG process requires good amount of surface grinding and fully avoidable in FCAW process.
It's economical compared to other processes in the long run.

C Sridhar,

Welding Consultant & Trainer.
Advance Institute of Welding Technology, 
Chennai. Tamilnadu.
e.mail: aiwttraining@yahoo.com,
           sridhar305@yahoo.com.
web:    advanceweldinginstitute.com







From: pgoswami <pgoswami@quickclic.net>
To: materials-welding@googlegroups.com
Cc: aggarwalmohit05@gmail.com
Sent: Sunday, 15 May 2016 9:04 AM
Subject: [MW:24799] RE: 24789] Regarding FCAW in SS

Hi Mohit,
 
FCAW is an established welding process for Stainless Steels. Kobelco is a leading manufacturer of many varieties of quality FCAW products. Feel free to read though this attachment.
 
Thanks.
 
 
Pradip Goswami, P.Eng,IWE
Independent Welding & Metallurgical Engineering Specialist & Consultant.
Ontario,Canada.
ca.linkedin.com/pub/pradip-goswami/5/985/299
pgoswami@quickclic.net
pradip.goswami@gmail.com
 
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Mohit Aggarwal
Sent: Saturday, May 14, 2016 12:49 AM
To: materials-welding
Subject: [MW:24789] Regarding FCAW in SS
 
Dear Experts,
Kindly let me know whether FCAW can be used in SS or not and if we can use then how much percentage of CO2 gas should be .
Regards,
Mohit Aggarwal
--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALTezPMcfhbT5UA_EChGO-eovO9rGQDWS4Zg3o1u_F7CV5O_TQ%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.
--
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/!%26!AAAAAAAAAAAYAAAAAAAAAOT5XfyRhstKvyeqQRSrfFXCgAAAEAAAAKaaXZ%2B4M8ZMmI2Ll1MQpDMBAAAAAA%3D%3D%40quickclic.net.
For more options, visit https://groups.google.com/d/optout.


Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

[MW:5202] RE: 5200] NDT after PWHT

By Materials & Welding
------------------------------------- Interpretation:  I‑89‑14 Subject:         Section I (1986 Edition, 1987 Addenda), PW‑11,                  NDE Prior to PWHT Date Issued:     December 15, 1988 File:            BC88‑393   Question: Does PW‑11 require that NDE be performed on welds after they have been subjected to the postweld heat treatment required by PW‑39?   Reply: No, unless the conditions described in PW‑11.2.2 exist. ---------------------------------------------- Interpretation:  VIII-1-98-09 Subject:         Section VIII, Division 1 (1995 Edition, 1996 Addenda); NDE                 ...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more