Re: [MW:23063] Clarification on Impact test of WPS and Prduction welds_ASME Sec 8 Div 1

Given combination is not exempted from Impact testing (Fig UCS-66M)
For PTC your designer need to classify (which category?) whether these are as per Fig UW13.2 or covered by U2(g) as angle joints (with α > 30 ° as per UW3)

On 9 June 2015 at 09:52, k c <kcrtechnical@gmail.com> wrote:
Dear Group Members,

Base Material : SA 516 Gr 70  
Thickness   : 60 MM
MDMT   : Minus 45 Deg C

Weld consumables Tested for Impact at Minus 46 Deg C
Code : ASME Section 8 Div 1
Joint : Corner Joints
Weld process : GTAW + SMAW + SAW

Designer says : Weld metal exempt as per UCS-67-a-3

Question :

Requirement of Impact test on WPS  ?
Requirement of Production test coupons ?


--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to materials-welding@googlegroups.com.
Visit this group at http://groups.google.com/group/materials-welding.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADxVub%3DrJ8LiKm5iwW4oou5XJT0bOpMVoJdMgk99pxNrha8ZwA%40mail.gmail.com.
For more options, visit https://groups.google.com/d/optout.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...