Re: [MW:23960] separate PQR for Fillet position like3F,4F or 2F required or not?

to be more accurate, when impact test is a requirement and you change from a given position to the vertical uphill position.
If the PQR was done on a vertical uphill progression then you do not need a new PQR even when impact test is a requirement

best regards

Dr. Georgios Dilintas

Authorized Nuclear Inspector
Authorized Inspector Supervisor

I&F REGIONAL TECHNICAL MANAGER
BUREAU VERITAS PIRAEUS - GREECE

Tel: +30 210 40 63 113 /4 /5
Fax: +30 210 40 63 118
Cell: +30 69 44 64 62 04


Kannayeram Gnanapandithan ---08/12/2015 10:00:11---Is there any impact requirements, if not, u need not do again, if it is there then u have to do

From: Kannayeram Gnanapandithan <kgpandithan@gmail.com>
To: materials-welding@googlegroups.com
Date: 08/12/2015 10:00
Subject: Re: [MW:23958] separate PQR for Fillet position like3F,4F or 2F required or not?
Sent by: materials-welding@googlegroups.com





Is there any impact requirements, if not, u need not do again, if it is there then u have to do

On 08-Dec-2015 10:40 am, "hasin shaikh" <hasin.shaikh@gmail.com> wrote:


--
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to
materials-welding+unsubscribe@googlegroups.com.
To post to this group, send email to
materials-welding@googlegroups.com.
Visit this group at
http://groups.google.com/group/materials-welding.
To view this discussion on the web visit
https://groups.google.com/d/msgid/materials-welding/CAJzm4eNv9pcK5q_kt5yRx1yCAM8vMDSJRjJGyn6nuqUG3PTj1A%40mail.gmail.com.
For more options, visit
https://groups.google.com/d/optout.

This message contains confidential information. To know more, please click on the following link: http://disclaimer.bureauveritas.com

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...