Re: [MW:35412] minimum thickness for Ultrasonic Testing (UT).

ASME Sec IX
QW-191.2 Ultrasonic Examination
QW-191.2.1 Method
(a) The ultrasonic examination in QW-142 for welders
and in
QW-143 for welding operators may be conducted
on test welds in material
14 in. (6 mm) thick or greater.
(b) Ultrasonic examinations shall be performed using a
written procedure in compliance with Section V, Article 1,
T-150 and the requirements of Section V, Article 4 for
methods and procedures.



Thank you, 
Regards, 
S.SENTHILKUMAR


On Thursday 30 January, 2025 at 11:20:15 am GMT+3, VIVEK DUBEY <vdubey183@gmail.com> wrote:


While ASME doesn't explicitly state a minimum thickness for weld plates undergoing UT testing, practical limitations and industry best practices generally dictate a minimum thickness of around 6 mm (1/4 inch).


Important considerations:
* ASME Section V, Article 4: This section provides guidelines for ultrasonic examination procedures, but doesn't specify a minimum thickness.
* Code cases: Some ASME code cases might allow UT on thinner materials under specific conditions.
* Other standards: Other standards, such as AWS D1.1 for structural welding, might provide guidance on minimum thickness for UT.
* Practical limitations: The actual minimum thickness that can be effectively inspected by UT can depend on factors like the material type, welding process, and the specific UT equipment and techniques used.
It's crucial to consult the relevant ASME codes, industry standards, and qualified NDT personnel to determine the appropriate minimum thickness for UT testing in your specific application.


On Thu, Jan 30, 2025, 1:22 PM P NAVEEN <pnaveen010@gmail.com> wrote:
Dear All,

What will be the minimum thickness of a weld plate required for UT testing as per ASME?  

Thanks,
P Naveen.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/48f49f35-2ebe-4a47-8361-103c629d3b66n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CALPqBbQfbwCb2wdcmS4JXYPzxz--yx%2BqZZpo-3kyU3keTSoA%3Dw%40mail.gmail.com.

No comments:

Re: [MW:35477] WPS for Furnace PWHT

The spools have 1" to 36" Piping joints. The WPS with PWHT is available only for large diameter / high thickness. can we do PWHT i...