Re: [MW:35371] Pipe 304L(P8) – Pipe 304L(P8)

308 L is for better corrosion resistance application,  But 308 H is for high temperature with minimum carbon control is maintained say 0.04, inferior to corrosion resistance. Ur Temp is not high. 

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015, ISO 3834, EN 15085, 

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Wed, Dec 25, 2024 at 1:01 PM Vinay <vinay.thattey@gmail.com> wrote:

Yes . E/ER 308L is having beter corrosion resistance  but strength reduces marginally. You can also try E/ER 308LM

On Mon, 18 Nov 2024 at 17:39, Marco Nunes <marcovsky82@gmail.com> wrote:

Can  anyone provide some assistance in the issue identified below:

The details are as follows:

 

Details

Parent material Pipe 304L(P8) – Pipe 304L(P8)

Inservice temperature range – 35-85 °C

Operating Pressure – 0.4 -0.5 MPaG

Process Type – Process Condensate.

Carbonic acid – there may be the presence of carbonic acid as indicated by CGCL.

 

Approved Process

WPS# P8-P8 AR - Filler material ER308L- F6 filler metal

 

Quality Issue

ER308H rods were used instead of ER308L on two locations of the 304L piping.

 

Technical Advice Request

The client indicated that the use of the ER308H Filler Wire instead of the ER308L has a higher risk of intergranular corrosion and corrosion related issues.  

 

Please advise on the short term or long-term quality effects on the integrity of the welded joints where the ER308H filler wire were utilized.

 

Thanking you in advance.

Mark Nunes

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAHXTn13_GqEVg7xyKfzH26pgfOGr8us4_2HTsfih1tPZn-vFwQ%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CA%2BQ29Oh5yaenUFNs4TGO8OCh7ix39xJHMJwiSzAbuNRQpmbAsg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eMSdVP9L96hSRZ%2BFEeJbjtPpnhb8GVMjYJj8JGE7b_SQQ%40mail.gmail.com.