Re: [MW:34040] Consumable Selection

Use 316Ti, for 6CrNiMoTi 17122. and for 13CrMo 4-5 either NiCr3 or 309 ( based on service Temp)

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Wed, Feb 22, 2023 at 9:12 AM Anand Elankumaran <email2uranand@gmail.com> wrote:

Dear Experts,

Could you Please advise if the below consumable selection is correct or not.

WPS Requirements as per BS EN 15609 & 15614
Material	Size	Process(Est. Weld thk)	Material Grouping  as per PD CR ISO 15608	Suitable Consumable		Remarks
				GTAW	SMAW
1.4571EN  X 6 CrNiMoTi 17 122 to 1.4571EN  X 6 CrNiMoTi 17 122	22.3 X 2.77	GTAW (2.77)	8.1	ER 316L-17	--	(Exaton 316/316L-17)
1.4571EN  X 6 CrNiMoTi 17 122 to 1.4571EN  X 6 CrNiMoTi 17 122	168.3 X 10.97	GTAW + SMAW (4 + 6.97)	8.1	ER 316L-17	E 316L-17	(Exaton 316/316L-17)
1.7335EN, 13CrMo4-5 to 1.4571EN X 6 CrNiMoTi 17 122	33.4 X 3.38	GTAW (3.38)	8.1 - 5.1	ER NiCrMo-3	--

 

--

Thanks and Regards,

E. Anand,

Lead QA-QC,

Sohar,

Oman.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CANOYChwvFgCTrAHGN4Jp62zbaUGPfo%3D2YjVi7Vn8y44q9eufcQ%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eNFMDnEksFYoUNmh%2BM%2Ba4LkFJpkWjhxWELKMX3WZ5%2B0WQ%40mail.gmail.com.