[MW:34073] Re: Guidance required

Thanks a lot

The PFHT for conditions prescribed in Code is well received.

I am seeking guidance for Monel cladded , SS 304 L base plate..

This (Monel cladding - 6 mm and SS 304L - 18 mm)needs hot forming due to thickness .

In view of operating conditions (Service temperature and Fibre elongation)PFHT is not required .

Hot forming at 1060 Deg C will be carried out for above plate and head will be formed .

Does Monel require some Annealing or not .? and so the composite plate formed Dished end - head

The Oxygen service is there at Tube side ( Channel shell and Dish end - head is Monel cladding with SS 304L as a base plate)

If yes, what will the temperature be ?

that was the query

Thanks once again

Vishwas - IWE

On Fri, Mar 17, 2023 at 6:40 PM P Goswami <pgoswami@rogers.com> wrote:

Hello Viishwas,

Please see the attached table for guidance on the temperature to be adopted for PWHT. In addition, please refer the clauses indicated with arrows to check the extent of staring in the formed component and consequently if the component would require any PFHT.

I'm posting this in the forum also, so that any additional guidance may be provided by any other knowledgeable person.

Hope this clarifies your doubt.

Best Regards.

Pradip Goswami.P.Eng, IWE.
Cell/Whasapp:1-905-9793232

From: Vishwas Keskar <vvkeskar123@gmail.com>
Sent: March 16, 2023 4:11 AM
To: P Goswami <pgoswami@rogers.com>
Subject: Re: Guidance required

Sir
This is an Oxygen pre heater HEX.
Tube side - Monel tubes and
Channel ,Dish - Monel

Process engineer has selected 304L + Monel 400
Rest are SS 304L

On Thu, Mar 16, 2023 at 9:17 AM P Goswami <pgoswami@rogers.com> wrote:
What's the service? Why 304L S.S is being overlayed with Monel 400?

Thanks.

Pradip Goswami.P.Eng, IWE.
Cell/Whasapp:1-905-9793232

From: Vishwas Keskar <vvkeskar123@gmail.com>
Sent: March 15, 2023 8:08 AM
To: pgoswami@rogers.com
Subject: Guidance required

Dear Sir
Good afternoon
I am very thankful to you for the guidance that is being provided to me for the fabrication/Metallurgy etc. .
Pl. guide for below .
,Background -
SS 304L -18 mm plate is cladded with MONEL 400 by explosion bonding.(6mm)
Ellipsoidal dished end is to be formed (570mm ID).

PFHT by virtue of operating conditions is not envisaged .

Seeking guidance for :
Pl. Suggest
1)Cold forming or
2) Hot forming

Pl. suggest suitable process/any heat treatment with supporting Code/Book reference

Thanks
Vishwas - IWE

Virus-free.www.avg.com

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADder3MVQo0fXSzNuzktLdbGqee2i9X5%3D-vVAEJ_gwHQM69pmg%40mail.gmail.com.

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...

Materials & Welding

Search This Blog