cheap and effective. Remember that, if you do go for an all-plastic tank,
you need to consider the possibility of impact damage and UV degradation, if
it is located outside.
Cheers,
Owen.
----- Original Message -----
From: "esharp" <eric.j.sharp@gmail.com>
To: "Materials & Welding" <materials-welding@googlegroups.com>
Sent: Tuesday, June 23, 2009 1:12 PM
Subject: [MW:2513] Brine Tank Material Selection
>
>
> I have an old carbon steel brine tank which is severly corroded and
> needs to be replaced. The brine solution contains ~ 10% salt (NaCl)
> and 1% caustic (NaOH) at 110 deg F. The tank is used intermittently in
> a batch process: filled for a few hours then drained and left empty
> for 2 days. It is open to the atmosphere.
>
> Initialy I was considering using 316 SS, but have been reading that
> pitting could be a problem with the chloride. What material should be
> used in this application?
>
> Thanks for your help.
>
> >
>
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
Comments