To weld SS 316 you should use matching SS consumable. It it is not a "L" grade material like SS 316L , you can use E316 for SMAW / ER 316 for GAW , & if the base material is "L" grade like SS 316L, you have to use E316L or ER316L, but even in both the cases you can use E316L / ER316L consumable.
Pre-heating & PWHT is not required for Austenetic Stainless steel ( SS 316 ). But if your working place is full of moisture or in rain condition, you can apply heat just to remove the moisture from the surface of the joint to be welded.
Regards,
On Mon, Jun 29, 2009 at 12:27 PM, sandy kumar <sandy001987@gmail.com> wrote:
Can any one tell me how to weld SS 316 to SS316 ?
--
Sukamal Naskar
Malaysia
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---
2 comments:
Why PWHT is not carried on SS material??? not mentioned.
could you please advise what is the consumption of filler wire (welding rod) and argon gas for welding 316L stainless steel metal