[MW:2581] Re: pci course

By Materials & Welding
I would agree - we have just had one of our team trained by NACE this year
 
Kerrie Christian
From: materials-welding@googlegroups.com [materials-welding@googlegroups.com] On Behalf Of Sachin Joshi [sachin.joshi@cgl.co.in]
Sent: Monday, 29 June 2009 14:29
To: materials-welding@googlegroups.com
Subject: [MW:2564] Re: pci course

Yes,
The paint inspection courses conducted by SSPC or NACE are honoured in Gulf countries but I would suggest to go for NACE as it is more evolved. I am sorry but that is my personal opinion and no offense towards SSPC as a society or technological expertise.
-Sachin

-----Original Message-----
From: andiappan pillai <sandiappan@yahoo.co.in>
Reply-to: materials-welding@googlegroups.com
To: materials-welding@googlegroups.com
Subject: [MW:2560] pci course
Date: Sun, 28 Jun 2009 06:31:51 +0530 (IST)

Does any one knows about , paint coating inspection conducted by sspc ,usa ? is it honored by gulf countries?. thanks in advance S.A.Pillai.


ICC World Twenty20 England '09 exclusively on YAHOO! CRICKET



NOTICE - This message and any attached files may contain information that is confidential, legally privileged or proprietary. It is intended only for use by the intended recipient. If you are not the intended recipient or the person responsible for delivering the message to the intended recipient, be advised that you have received this message in error. Any dissemination, copying, use or re-transmission of this message or attachment, or the disclosure of any information therein, is strictly forbidden. BlueScope Steel Limited does not represent or guarantee that this message or attachment is free of errors, virus or interference.

If you have received this message in error please notify the sender immediately and delete the message. Any views expressed in this email are not necessarily the views of BlueScope Steel Limited.
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more