Hi

You can also repair with Eutectic Castolin, Maintenace & Repair SMAW Electrode: 300DC+ with proper preheating @250 degrees C.

Regards

Prem Nautiyal
Godrej, Mumbai.

On Wed, 24 Jun 2009 21:04:26 +0530 wrote
>It is a structural repair! All the structure is in copper, is a very old statue.
>
>thanks
>monica
>
>________________________________
>
>De: materials-welding@googlegroups.com em nome de T. Paul Coley
>Enviada: qua 24/6/2009 11:17
>Para: materials-welding@googlegroups.com
>Assunto: [MW:2530] Re: copper
>
>
>
>
>Depends on what the repairs are ... is it a structural repair or cosmetic? What material is the main structure? Is this copper sheeting, or overlay, which is thinner. We'll need more data
>
>T.
>
>--- On Wed, 6/24/09, monica wrote:
>
>
>
>   From: monica
>   Subject: [MW:2529] copper
>   To: "Materials & Welding"
>   Date: Wednesday, June 24, 2009, 10:11 AM
>   
>   
>
>   Hi,
>   
>   I have a big copper statue (monument) that i need to repair. which is
>   the best welding?
>   
>   thanks,
>   monica
>   
>   
>      
>   
>
>
>>
>As informaes existentes nesta mensagem e nos arquivos anexos so para uso restrito e confidencial, sendo seu sigilo protegido por lei. Se voc a tiver recebido por engano, por favor, notifique imediatamente ao remetente e remova a mensagem e qualquer anexo de seu sistema. O Sistema FIRJAN no se responsabiliza por qualquer omisso ou falhas contidas nesta mensagem, que possam surgir na transmisso da mesma ou por prejuzos provenientes de quaisquer alteraes de seu contedo. Esta mensagem © de responsabilidade de seu autor e seu contedo no reflete, necessariamente, a opinio da empresa.
>

PREM S NAUTIYAL

CELL : 9820313278
--~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

[MW:5202] RE: 5200] NDT after PWHT

By Materials & Welding
------------------------------------- Interpretation:  I‑89‑14 Subject:         Section I (1986 Edition, 1987 Addenda), PW‑11,                  NDE Prior to PWHT Date Issued:     December 15, 1988 File:            BC88‑393   Question: Does PW‑11 require that NDE be performed on welds after they have been subjected to the postweld heat treatment required by PW‑39?   Reply: No, unless the conditions described in PW‑11.2.2 exist. ---------------------------------------------- Interpretation:  VIII-1-98-09 Subject:         Section VIII, Division 1 (1995 Edition, 1996 Addenda); NDE                 ...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more