This is Carbon steel . Should not be any issue with L seam soundness.

Pl repeat NDT 

Thanks 

Vishwas  -IWE

9823472273

Sent from my iPhone

On 27-Sep-2023, at 7:22 PM, RAJESH KUMAR <rajeshkumarbhaskara@gmail.com> wrote:



Dear Expert,

During a site observation, a subcontractor's carbon steel shell (EH36, thickness 40 mm) was found re-rolled due to ovality after 100% of the NDT(UT&MPI) long seam welds. Many stresses come and grain boundaries are stretched after rolling such a thick joint.Any experts please advise.

Standard - DNV-OSC -401
Construction specifications - AWS D1.1

<image.png>

Thanks & Regards

Rajesh

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAMtcSfO5WESSOFt_GNicQH25ffSSuAHHGSSfNkCMp2FRCzLAMQ%40mail.gmail.com.