Re: [MW:35412] minimum thickness for Ultrasonic Testing (UT).

By Materials & Welding
ASME Sec IX
QW-191.2 Ultrasonic Examination
QW-191.2.1 Method
(a) The ultrasonic examination in QW-142 for welders
and in QW-143 for welding operators may be conducted
on test welds in material 1∕4 in. (6 mm) thick or greater.
(b) Ultrasonic examinations shall be performed using a
written procedure in compliance with Section V, Article 1,
T-150 and the requirements of Section V, Article 4 for
methods and procedures.


Thank you, 
Regards, 
S.SENTHILKUMAR


On Thursday 30 January, 2025 at 11:20:15 am GMT+3, VIVEK DUBEY <vdubey183@gmail.com> wrote:


While ASME doesn't explicitly state a minimum thickness for weld plates undergoing UT testing, practical limitations and industry best practices generally dictate a minimum thickness of around 6 mm (1/4 inch).


Important considerations:
* ASME Section V, Article 4: This section provides guidelines for ultrasonic examination procedures, but doesn't specify a minimum thickness.
* Code cases: Some ASME code cases might allow UT on thinner materials under specific conditions.
* Other standards: Other standards, such as AWS D1.1 for structural welding, might provide guidance on minimum thickness for UT.
* Practical limitations: The actual minimum thickness that can be effectively inspected by UT can depend on factors like the material type, welding process, and the specific UT equipment and techniques used.
It's crucial to consult the relevant ASME codes, industry standards, and qualified NDT personnel to determine the appropriate minimum thickness for UT testing in your specific application.


On Thu, Jan 30, 2025, 1:22 PM P NAVEEN <pnaveen010@gmail.com> wrote:
Dear All,

What will be the minimum thickness of a weld plate required for UT testing as per ASME?  

Thanks,
P Naveen.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/48f49f35-2ebe-4a47-8361-103c629d3b66n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CALPqBbQfbwCb2wdcmS4JXYPzxz--yx%2BqZZpo-3kyU3keTSoA%3Dw%40mail.gmail.com.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more