Excess weaving will tend to rise Heat input more so, Toughness will be reduced. Mechanical property will change as said above. 

On Mon, Oct 2, 2023, 15:59 RAJESH KUMAR <rajeshkumarbhaskara@gmail.com> wrote:

Dear Experts,

Code:BSEN 15614-1:2017 ,BSEN 15609:2019 and DNV-OS-C401

I have noticed that WPS says the weaving is allowed/permitted 18 mm maximum for FCAW welding process.Please tell me whether we can allow if the weaving is more than the allowable limit.If it can be allowed.What is the reasons and on what basis it is allowed?If it can not/should not be allowed.Why and what is the reasons?

Thanks & Regards

Rajesh kumar

Dubai.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAMtcSfPVaUrZpa-zbt1cQ0%3DcLD5g6OuEVPkDv36KTkbeZUsghg%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CALUa47he2Ae7kxHkjsUYt4HEQQBC1_S6UYMrZv%3DOyCT-GgqGoA%40mail.gmail.com.