Re: [MW:35818] Material SA 335 P9 (P No. 5B) Welding with ER 80S-B8 or ER90S-B91

By Materials & Welding
Dear Sir,

SA335 P9 is a highly weldable material. We have successfully completed a job for EIL using this material and have the relevant WPS PQR and PWHT documentation for P9.

We would be happy to share these with you if you are interested.

Regards,


Chandrakant
B.E Mech.
ASNT Level II RT/UT/PT/MPT/CSWIP
Patni Engineers. Mumbai. India
PED/2014/68/EU
welding shop AD2000/DIN EN ISO 3834
IBR Approved 

Factory Addreess- Pl Call 

On Mon, 15 Sept 2025, 23:10 venkateswara reddy Desireddy, <dvreddy82@gmail.com> wrote:
Weld joint Post weld heating 100°C one hour should be maintained. 
Electric coil heating is preferred to maintain proper temperature.
Based on thickness PWHT to be done. 
To ensure weld quality go for helium leak test. 

From: materials-welding@googlegroups.com <materials-welding@googlegroups.com> on behalf of Ch Bilal jovinda <chbilaleng1989@gmail.com>
Sent: Monday, September 15, 2025 8:09:58 PM
To: materials-welding@googlegroups.com <materials-welding@googlegroups.com>
Subject: [MW:35814] Material SA 335 P9 (P No. 5B) Welding with ER 80S-B8 or ER90S-B91
 
Dear Group Members,

We are working with material SA 335 P9 8mm thickness, which has a P number of 5B. For welding this material, we are using consumables ER 80S-B8 or optionally ER90S-B91.

I would like to request members who have experience welding with ER 90S-B91 (closely related to ER90S-B9) to share any necessary precautions or considerations that should be taken during welding.refere below we are taking care,

1.Preheat to 210 degree centigrade minimum.
2. Interpass 300 degree centigrade maximum.
3. What are other recommended?

Best regards,
Bilal Chauhadry,

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAOq7hqvpGAzaQ3urEHdwMRqn94bMZ-12BOsL0tkmmkLFLDFFNA%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/PARP264MB6204923EB91E147438F71694AA15A%40PARP264MB6204.FRAP264.PROD.OUTLOOK.COM.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CAKLNAG7Mp-ev95nOwpkfh52G%3D5nn_komvXzAd0p8z3xO%2B%3DxU2A%40mail.gmail.com.

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more