Some basic understanding on code reading, In B31.3 they have simply mentioned about material thickness, P No and group no which is interlink with each other in one table and below is code statement.
Check also about CEV for PWHT.
Regards,
--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/7a31474b-44ca-4add-a615-3a6015d41906n%40googlegroups.com.
331 HEAT TREATMENT
331.1 General
331.1.1 Postweld Heat Treatment Requirements ð18Þ
(a) PWHT shall be in accordance with the material
groupings (P-Nos. and Group Nos.) and ranges in
Table 331.1.1 except as provided in Table 331.1.2 and
Table 331.1.3. See Appendix F, para. F331.1. The P Numbers
and Group Numbers are defined in ASME
BPVC, Section IX, Table QW/QB-422. (Note that the PNos.
are also listed in Appendix A.)
It means all factor shall be always taken in to consideration and not any particular. Check also about CEV for PWHT.
Regards,
On Thursday, September 9, 2021 at 9:17:38 AM UTC+3 senins wrote:
Dear all,Pls I needs your all valuable comments regarding PWHT thickness,As per ASME B31.3 2018,Table 331.1.1, whether PWHT based on thickness of base metal or P.No and Group No,I appreciate your guidance,SENTHIL P
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/7a31474b-44ca-4add-a615-3a6015d41906n%40googlegroups.com.
Comments