Re: [MW:35998] Group number selection when toughness requirement is there

By Materials & Welding

Snap shot from ASME Sec.IX
Inline image


Thanks & Regards

J.Gerald Jayakumar

0091-8838619635



On Friday, 6 February 2026 at 03:32:29 pm IST, 'Birupakhya Sahu' via Materials & Welding <materials-welding@googlegroups.com> wrote:


Yes , It is acceptable with G1 to G1 & G2 to G2 subject to HAZ Impact test required to perform for both HAZ G1 & G2 in PQR.

Regards,
Birupakhya Sahu
TEMA India Private Limited, 
Kherdi, Silvassa (D&NH).



On Fri, Feb 6, 2026 at 2:23 PM praba karan <prabakaran776@gmail.com> wrote:
Dear Experts,

Need your clarification on the following,

When the PQR(GTAW+SAW) is qualified with (Pno-1 Group no 1) with (Pno-1 Group no 2).-With impact test.

As per Sec IX, G number will be essential variable when toughness requirement is there, So can i prepare WPS for the same p number and same group number within themselves?
Like, 1)  Pno1, Group no 1 to Group no 1
          2)  Pno1, Group no 2 to Group no 2,

or is there any other suggestions to cover all groups?

Thank you..

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/90d39d5b-a8b3-4492-953d-c766aa71432en%40googlegroups.com.



​_____________________________ ______________________________ ______________________________ ______________________________ _________ ​
This email (including any attachment(s) hereto) contains confidential or privileged information intended solely for the designated individual or entity to whom it is addressed. If you are not the intended recipient, please delete this message permanently and notify the sender immediately. Any unauthorized use, disclosure or distribution is strictly prohibited. TEMA India Pvt Ltd is not liable for the improper transmission of this message or any damage sustained as a result of it.
​ ​_____________________________ ______________________________ ______________________________ ______________________________ _________

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion visit https://groups.google.com/d/msgid/materials-welding/CANbQDEyUdQPxk4x3Yq_0qAKt6fe40q5DvmEPfo8jUOn%2B9FGyqQ%40mail.gmail.com.

Comments

Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

The Schaeffler and Delong diagrams for predicting ferrite levels in austenitic stainless steel welds

By Materials & Welding
Introduction Ferrite is important in avoiding hot cracking in during cooling from welding of austenitic stainless steels. 'Constitution diagrams' are used to predict ferrite levels from the composition by comparing the effects of austenite and ferrite stabilising elements. The Schaeffler and Delong diagrams are the original methods of predicting the phase balances in austenitic stainless steel welds. Nickel and chromium equivalents A 'nickel equivalent' is calculated for the austenite stabilising elements and a 'chromium equivalent' ferrite stabilising elements. These are used as the axes for the diagrams, which show the compositional equivalent areas where the phases austenite, ferrite, martensite (and mixtures of these) should be present. Although intended to show the phase balance of weld fillers, these diagrams can also be used to illustrate the phase balance of the 'parent' material. There are different diagrams for dif...
Post a Comment
Read more