Re: [MW:32580] SA 516 GR 70- AVOIDANCE OF PWHT - 40 mm thickness

Please experts to share on Designer's view with respect to different lateral expansion though Design temperature is +250degC

Thanks & Regards

J.Gerald Jayakumar

On Friday, 29 October, 2021, 11:53:02 am GMT+4, Vishwas Keskar Welding Manager WELDING <vvkeskar123@gmail.com> wrote:

The vessel details are 

MOC - SA 516 GR 70 

DIAMETER- 4020mm

LENGTH - 37 MTR

MDMT = - 50 Deg C to  + 250 Deg C 

SERVICE - Non lethal /No Hydrogen Service 

We are proposing Vessel length build up as per FURNACE LENGTH CAPACITY(24 m maximum) and one joint WITHOUT PWHT  ( JOINING PWHTed sections earlier at site )

Proposal - 

1.MOC - SA 516 GR 70 

2.BUTTERING - ENiCrFe2 on 24 m section end and other at 13 m section end)

3,PWHT (section PWHT - One of 24  length and other 13 m)
 of  - 620 Deg C - 125 MINUTES 

4.Bevel preparation 

5.NDT - DPT 

Welding at site ( 24 m section with 13 m section) - ENiCrFe2 OR E309 

6.NDT - DPT AND UT

Expert opinion please  and share experience if any 

Vishwas 

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/bdca7c90-9d2b-4df4-a685-5e7745a76351n%40googlegroups.com.