Re: [MW:31986] ASME B31.3_2018- Table 331.1.1-PHWT minimumn Holding Time for base material thk-75mm

Why they segregated as group and in which basis ?

On Thu, 4 Feb 2021, 08:31 Anban, <gane2478@hotmail.sg> wrote:
Dear Experts

Need your guidance in understanding  PWHT minimum  Holding Time base material thk.-65 ~ 75mm

P-No. 1, Group Nos. 1–3
Minimum Holding Time at Temperature for Control Thickness [Note (2)]
-Up to 50 mm (2 in.)-1 h/25 mm (1 hr/in.);15 min min.
-Over 50 mm (2 in.)-2 hr plus 15 min for each additional 25 mm (in.)


Best Regards
Ganesan

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/b538da9f-4e78-4b7c-85c3-7679328ed9bdn%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAGWOcnqMNXcWFH-bUvTt7GM1yoJJC6o5fUR_aKy3aWTuQs5fPQ%40mail.gmail.com.

No comments:

Re: [MW:35289] Welding consumable for S355J2WP material

S355 J2 WP  is a weathering structural steel  It has better atmospheric corrosion resistance. Use E 8018 - W1/W2  Electrodes This is regular...