Materials & Welding

Sirs, Do we have supporting verses in ASME? Thanks On Thursday, May 16, 2024 at 5:58:42 PM UTC+8 Mohamed Ali wrote: Kindly get client specification for the same as they have mentioned the acceptance criteria in the same. Many clients are acceptable the tolarnce range is +- 10%. In this case Chromium range between 19.8 to 28.6 is acceptable.  On Thu, 16 May 2024, 11:53 am Ahmed Fouad, < dah...@gmail.com > wrote: You can make a weight analysis to insure the real content of Cr. Knowing that this test is a destructive test. thank you ‫في الخميس، 16 مايو 2024 في 9:35 ص تمت كتابة ما يلي بواسطة ‪Macario Jr. Palola‬‏ <‪ macario...@gmec.ph ‬‏>:‬ Sirs, May I ask your valuable inputs with regards to my queries. Base on the attached report, the actual value of %Cr is 20% as per PMI and the value of %Cr in ASME Sec IIA. Now my question, is this acceptable or not ? Thank you in advance. Regards, Mac The information contained in this email is intended for use only by the recipient t...

Dear team    What is impact test? , what is the reason to do that?, how to select impact temperature for each material?,  Non aramco and aramco  Thanks & Best Regards Saleem manhappulath Mob:+966533595849 WhatsApp:+919526445936 From iPhone xs -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKH3Omv%3DVHBp6v-XuNWuJQuq%2B9waiwKmixJbJFNCQ68%3DGLwyGw%40mail.gmail.com .

MDMT  On Fri, May 17, 2024 at 9:50 AM saleem manhappulath < saleemm9526@gmail.com > wrote: Dear team    What is impact test? , what is the reason to do that?, how to select impact temperature for each material?,  Non aramco and aramco  Thanks & Best Regards Saleem manhappulath Mob:+966533595849 WhatsApp:+919526445936 From iPhone xs -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKH3Omv%3DVHBp6v-XuNWuJQuq%2B9waiwKmixJbJFNCQ68%3DGLwyGw%40mail.gmail.com . -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message b...

Refer ASME SEC VIII DIV1 UCS 66  On Fri, 17 May 2024, 9:50 am saleem manhappulath, < saleemm9526@gmail.com > wrote: Dear team    What is impact test? , what is the reason to do that?, how to select impact temperature for each material?,  Non aramco and aramco  Thanks & Best Regards Saleem manhappulath Mob:+966533595849 WhatsApp:+919526445936 From iPhone xs -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAKH3Omv%3DVHBp6v-XuNWuJQuq%2B9waiwKmixJbJFNCQ68%3DGLwyGw%40mail.gmail.com . -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- Yo...

Greetings Experts, I would like to know more about PQR qualifications for Boiler tube material EN 10216-2 16Mo3 or SA 209 T1 with 6.5mm Thick, Welding Consumable : Should  I qualify the above material with ER80S-B2/ E8018-B2 or ER80S-D2 / E7018-A1, or which consumable is suitable for high temperature service like Boiler. PWHT : As per ASME SEC.I & VIII PWHT is not mandatory for P. No.1 Gr.1 up to 16mm Thick and the Boiler tube and weld joints will undergo the Stress Relieving after tube bending as a coil. in this case Should i qualify the PQR with PWHT or Without PWHT. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.co...

Please refer ASME IIA  SA-370   /  ASTM A 370 Thanks & Regards J.Gerald Jayakumar 0091-8838619635 On Friday, 17 May, 2024 at 09:50:11 am IST, saleem manhappulath <saleemm9526@gmail.com> wrote: Dear team    What is impact test? , what is the reason to do that?, how to select impact temperature for each material?,  Non aramco and aramco  Thanks & Best Regards Saleem manhappulath Mob:+966533595849 WhatsApp:+919526445936 From iPhone xs -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an e...

Plz refer attach  Thank and regards Dinesh Baskaran On Thu, 16 May, 2024, 12:05 pm Macario Jr. Palola, < macario.palola@gmec.ph > wrote: Sirs, May I ask your valuable inputs with regards to my queries. Base on the attached report, the actual value of %Cr is 20% as per PMI and the value of %Cr in ASME Sec IIA. Now my question, is this acceptable or not ? Thank you in advance. Regards, Mac The information contained in this email is intended for use only by the recipient to whom or which this is addressed. Such information may be privileged, confidential, and/or proprietary subject to the GMEC Email Disclaimer.   Moreover, as we value your privacy, we will handle and safeguard any personal data we receive in this email in accordance with our Privacy Notice. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group...