Re: [MW:32723] QW 200.4: Combination of Welding Procedures

Basically 13mm changed from Weld metal thickness to Base Metal thickness and qualified weld metal thickness is 2t.

Thanks & Regards

J.Gerald Jayakumar

On Wednesday, 29 December, 2021, 03:10:27 pm GMT+4, Kannayeram Gnanapandithan <kgpandithan@gmail.com> wrote:

There is revision made in QW 200.4, 2021 edition. 

In 2019, it is clearly mentioned that when combination is made, the process which is going to be used for Root pass, shall have qualified at least 13mm thick.

In 2021, it is not specific about root pass process qualification thickness, but it is clear that u can combined/individual the process in  which each combined or individual might have been qualified at least on 13mm thick. 

If any of process is not qualified on 13mm thick, shall not be combined. any process can be used for root pass with max 2t and another one with maximum base metal thick.

THANKS & BEST REGARDS,

KG.PANDITHAN, BE, IWE,  CSWIP 3.1,

ISO 9712 Level 2 in VT,

ASNT-Level II in PT,MT,RT & UT,

LA ISO 9001-2015,

International Welding Engineer. 

CONSULTANT-WELDING & QUALITY

Mobile no: +919940739349

On Wed, Dec 29, 2021 at 9:05 AM Sudhakar Kuppuswamy <sudhakarceng@gmail.com> wrote:

Hi,

Currently one of my clients is having an ambiguity in applying the requirements of ASME Section 09 Clause QW 200.4: Combination of Welding Procedures, Subclause:  a & b requirements. Hence, support is required in finding an interpretation from ASME Section 09. (Interpretation in CS connect is not apparent for this clause)

Background: Two PQRs were qualified separately, PQR A is qualified with SAW process using 8 mm thickness plate and PQR B is qualified with SMAW process using 8 mm thickness plate.

Question: While combining the two PQRs to weld a plate with thickness(es) ranging from 1.5 mm to 16 mm.

Do as per QW 200.4, it is necessary to have the root pass process PQR need to be qualified on a minimum 13 mm thickness plate?

I'm pretty sure it is not required to have a root pass process PQR with minimum 13 mm thickness in the above case. However, it would be helpful if you found any interpretation on this.

Regards,

Sudhakar K CEng MWeldI,IWE.

Welding & Metallurgical Engineer,

Email: sudhakarceng@gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CABF8NYVXu5Nu5k5yKnxevQH8xhLhEqjw0Fw7z0ogm--MNr-F-A%40mail.gmail.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CAJzm4eP7avyONq_9LgO-jHnv-pdG4hwLPuLC-w2q6Kf0ccJHHQ%40mail.gmail.com.