By Materials & Welding
In the above query the thickness of weld neck & nozzle has not been mentioned and assume that the connection is between the nozzle pipe & weld neck flange.If there is no PWHT as per design requirements then root  as well as final pass welding can be carried out using ER347 +E347 due to homogeneuous layer present. Welding final layer with Inconel will not give have any positive impact rather the chance pf cracking is not ruled out due to differential thermal expansion of P11+SS347+Inconel.Either full welding with 347 or Inconel will be a better option.
 
with regards,
gopalsanakr
DM(ES-Inspn)
CPCL
Chennai

"Bathula Raghuram (Mumbai - PIPING)" <R.Bathula@ticb.com> wrote:
Is this vessel subjected to PWHT?
I assume it should be, also assuming it is a stub in type connection, then use ER347 + E347  for joining weld overlay portion to LWN (i.e inside weld of nozzle), and may use Inconel consumables ERNiCr3+ENiCrFe-2/3 for weld on ouside (i.e fillet joining P11 to F321 neck)
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Desai Jignesh
Sent: Tuesday, January 29, 2008 2:46 PM
To: materials-welding@googlegroups.com
Subject: [MW:533] Filler metal for P 11 (O/L SS 347) to P8
 
Dear Member,
 
Can some body give his/her opinion for filler metal of following condition?
 
Branch connection (Tube Side) between LWN flange (Material SA 182 F321) to SR Nozzle (SA 182 F11 CL 2 + Weld Deposit 347 SS).
 
Service is Hydrogen.
 
Operating Wall Temperature - Tube Side is IN 372 C & Out 225 C.
 
Also recommend the filler metal for the first layer of weld deposite.
 
Thanks in advance
 
Jignesh
 


Looking for last minute shopping deals? Find them fast with Yahoo! Search. --~--~---------~--~----~------------~-------~--~----~
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding-unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
-~----------~----~----~----~------~----~------~--~---

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

[MW:36169] Cold Bending Qualification

By Materials & Welding
Dear Experts,  Can anyone share the inspection requirements or a qualification procedure for cold bending? Our client spec states only the requirements for induction bending and would like to know your opinion on the cold bend inspection requirements. The code of construction is B31.3, Max. 5D bends, A106 SS 316L.  Thanks in Advance. -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion visit https://groups.google.com/d/msgid/materials-welding/1be61cc3-e9c9-4a5f-834d-e8485e248432n%40googlegroups.com .
Post a Comment
Read more

[MW:30043] Weep hole

By Materials & Welding
If weep hole is not provided in dummy pipe before welding What will happen??? -- https://materials-welding.blogspot.com/ https://www.linkedin.com/groups/122787 --- You received this message because you are subscribed to the Google Groups "Materials & Welding" group. To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com . To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/da251ee6-fa7f-4851-b876-cdb3834ae341%40googlegroups.com .
Post a Comment
Read more