Let us know what  is P NO of  PQR ?

On Mon, 16 Aug 2021, 08:46 Raja, <krajapandiyan@gmail.com> wrote:

i have some doubts in WPS, if possible kindly clarify me

1) If PQR is done with Normalization heat treatment (PWHT done above the upper critical temperature), what is the qualified base metal thickness range to be taken ( min to max ) any special condition applicable in ASME Sec IX?

2) When Impact test is applicable to the WPS, then what is the qualified base metal thickness range to be taken ( min to max ). any special condition in ASME Sec IX?

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/0e6d52d2-c48a-4159-bf6f-88511b0a5ff6n%40googlegroups.com.

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/CADder3MG%2BAx-26Gs76W7nH1b%2B-3-6txYx%3D13y%2BKSpvZ6QJONSQ%40mail.gmail.com.