Single layer electroslag strip cladding of alloy 316L and 317L

1. Alloy 316L

Among the Cr-Ni stainless steel alloys, alloy 316L is one of the most widely used in the chemical and offshore industry.

For economic reasons, it is evident that single layer solutions are preferable and this can only be achieved by the use of the electroslag strip cladding process.

Today, Soudokay can offer two different, unalloyed electroslag fluxes allowing to reach the 316L chemical analysis in a single layer in combination with Soudotape 21.13.3L welding strip. The two solutions are summarized in the next table

Data

Both solutions offer a high quality deposit with an excellent wettability and smooth overlapping.

The <high speed> solution with Record EST 136 is recommendable while:

  • Deposition rate increases with ±20%
  • Surface coverage (m2/h) increases with ±35%
  • Consumption of consumables decreases with ±20%

2.Alloy 317L

This modified 316L alloy can be achieved by the use of Record EST 122Mo and Soudotape 21.13.3L.

Record EST 122Mo is a Mo-alloyed flux in order to guarantee min. 3% Mo in the single layer deposit.

Data 2

It is of course of outmost importance to make a 3/16 inch deposit in order to guarantee a Mo-content of 3% in the deposit.

3. Conclusions

The single layer deposits of 316L and 317L offer maximum results with minimum overlay thickness and is achieved by using our special strip, Soudotape 21.13.3L and electroslag cladding Record EST122 and Record EST122Mo.

Data 3

http://www.btwusa.com/html/ppf7.html

Comments

JASPAL SINGH said…
The ferrite content problem is there which is always required to be between 3-10.
December 3, 2008 at 11:09 AM
Post a Comment

Popular posts from this blog

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

[MW:5202] RE: 5200] NDT after PWHT

By Materials & Welding
------------------------------------- Interpretation:  I‑89‑14 Subject:         Section I (1986 Edition, 1987 Addenda), PW‑11,                  NDE Prior to PWHT Date Issued:     December 15, 1988 File:            BC88‑393   Question: Does PW‑11 require that NDE be performed on welds after they have been subjected to the postweld heat treatment required by PW‑39?   Reply: No, unless the conditions described in PW‑11.2.2 exist. ---------------------------------------------- Interpretation:  VIII-1-98-09 Subject:         Section VIII, Division 1 (1995 Edition, 1996 Addenda); NDE                 ...
Post a Comment
Read more

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more