The history of NACE MR-0175, ISO 15156, and the 1% nickel limit - Timeline

Studying complex phenomena such as sulfide stress cracking (SSC) of carbon and low alloy steels (LAS) requires a holistic historical perspective. For example, understanding the influence of microstructure on SSC resistance was made possible thanks, in part, to advances in electron and transmission electron microscopy. Since the early SSC failures that affected oil and gas equipment short after World War II,[1]-[2] much of our understanding of the underlying failure mechanisms as well as industry regulations matured in parallel with improvements in characterization techniques and new discoveries in the realm of physical metallurgy and corrosion. Nevertheless, the fundamental assumptions that led to the development of international standards such as NACE MR-0175 and ISO 15156 have more or less remained unchanged since their introduction more than 40 years ago. The persistence of the restriction in the allowable nickel content, the sole focus on hardness and strength limits rather than controlling causative factors such as the presence of untempered martensite illustrate this disjunctive quite well.

A historical perspective

I have recently started to compile a timeline describing the key events that catalyze the development of the NACE MR–0715 specification as well as the fundamental research that exploded as a consequence of recurrent failures and global standardization activities. I hope to gain a better understanding not only on SSC of LAS but also on the reasons that led to certain controversial decisions in standardization committees. 

Although it is a still a work in progress, I like to share the timeline with the community. I would very much like to get feedback from anyone working in this area, in particular from people that might have been involved in early research and NACE committee discussions. 

The timeline is embedded below and, thanks to the magic of the cloud, it will always be up-to-date. The entries can be expanded or collapsed for better viewing. There are a basic search function as well as zoom and panning tools. The full-screen version can be accessed HERE

References

1.     D.E. Milliams, R.N. Tuttle, “ISO 15156/NACE MR0175 - A New International Standard for Metallic Materials for Use in Oil and Gas Production in Sour Environments,” CORROSION 2003,  paper no. 03090 (16–20 March, San Diego, CA: NACE International, 2003).

2.     Patrick, D. H.,“MR0175 - A History and Development Study,” CORROSION 99, paper no. 418 (25–30 April, San Antonio, TX: NACE International, 1999).

Source: https://www.aboutcorrosion.com/

Comments

Popular posts from this blog

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...