Re: [MW:35169] RT selection Criteria for API 650 tank

By Materials & Welding
Dear expert 

please guide , what it means to  25 % of which shall be at intersections.

Best Regards,
Abd Ur Rehman
QA/QC Engineer
On Friday, November 8, 2013 at 4:19:23 PM UTC+5 Devang Majithia wrote:

 

Extract taken from API 650. Refer Figure 8.1

 

Regards

Devang Majithia

 

From: material...@googlegroups.com [mailto:material...@googlegroups.com] On Behalf Of Perumal Govindan
Sent: Thursday, November 07, 2013 11:28 PM
To: material...@googlegroups.com
Subject: Re: [MW:19199] RT selection Criteria for API 650 tank

 

Mr. Sam,

Review the MTC of plate material and tolerance of specific heat / lot number and then identify the thickness of the lowest shell course thickness.

 

For lowest shell course, one spot radiography on every vertical joint.

 

Hope this will clarifies your doubt.

 

P Govindan   

On Thu, Nov 7, 2013 at 4:52 AM, Mervin <mervi...@yahoo.com> wrote:

Dear mr sam

 

You can refer the api-650 clause 8.1.2.2 a&b and 8.1.2.3 as mention on this paragraph only spot RT for vertical & horizontal in the 1st 3mter and we use the standard in aramco for intersection joints on top angle to shell.

 

Vin

 



Sent from my iPhone


On Nov 6, 2013, at 9:54 AM, Sam <onlypri...@gmail.com> wrote:

Dear experts,

 

please guide me exactly how many percentage and which area i should select for RT for API 650 tank for below joints.

 

1) shell verticle

2) shell horizontal

3) shell intersections (verticle to horizontal)

4) nozzles

 

i checked API 650 but not getting clear picture hence request to provide standard practice in this regard.

 

regards,

sam.

 

--
To post to this group, send email to material...@googlegroups.com
To unsubscribe from this group, send email to materials-weld...@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

--
To post to this group, send email to material...@googlegroups.com
To unsubscribe from this group, send email to materials-weld...@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/


 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

--
To post to this group, send email to material...@googlegroups.com
To unsubscribe from this group, send email to materials-weld...@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-weld...@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.

Legal Disclaimer :  http://mail.gnfc.in/disclaimer

--
https://materials-welding.blogspot.com/
https://www.linkedin.com/groups/122787
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
To view this discussion on the web visit https://groups.google.com/d/msgid/materials-welding/5b83e661-0620-4813-a52d-b1322a9dd82an%40googlegroups.com.

Comments

Post a Comment

Popular posts from this blog

Materails FAQs

By Materials & Welding
Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...
21 comments
Read more

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

By Materials & Welding
Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change.   Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...
Post a Comment
Read more

Re: [MW:10788] ON PLOT PIPING & OFF PLOT PIPING

By Materials & Welding
Piping systems involved for the flow lines and gathering lines from the well head isolation valve to the production facility or processing plant isolation valve are determined as OFF PLOT. ON PLOT defines piping system in the processing plant and production platform. ANSI/ASME B31.4 applies for off plot piping system. B31.4 allows the use of either API 1104 or ASME section IX (as appropriate). However, occasionally, a very small system such as piping within 500 feet of a processing plant (some client also said 400 feet) may be declared B31.3 rather than B31.4. When B31.3 is invoked, only ASME Section IX is used. before you decide which code to use for welding procedure and/or welder qualification for pipe welding, you have to know the design and construction code applicable to the system. Please read far enough into scope and diagram illustrating the application of either B31.3 and B31.4 hope this helps rgds 2011/4/21 pradip kumar sil < pradipsil@gmail.com > Dear all, ...
Post a Comment
Read more