ASME B31.3 has the following major factors to recommend PWHT:
- Thickness- Alloy chemistry yielding in higher carbon equivalent (hardenability)
- Tensile strength
Octane
On Wed, Oct 16, 2013 at 1:34 PM, Ramin Kondori <raminkondori@gmail.com> wrote:
Dear swapnil:
In ASME B31.3 the requirement for PWHT is mainly to reduce welding residual stress and prevent cracking (even before service).
PWHT may be enforced for other reasons.
- In sour service piping, some specifications require PWHT for all welds. The reason is with reducing the weld residual stress, you will reduce the risk of corrosion especially where SCC is involved.
- Sometimes you need to reduce the hardness level and this will be achieved by PWHT (carbon steels etc.).
- It may be a part of low temperature requirements. LTCS piping welds shall be post-weld heat treated regardless of thickness otherwise HAZ toughness will not meet the minimum requirements.
- Sometimes you need to apply PWHT to complete production process for precipitation hardening materials which need some kind of tempering or aging to reach their full potentials.
The list can be a long list but above mentioned examples will cover many applications.RegardsOn Wed, Oct 16, 2013 at 10:09 AM, swapnil gorantiwar <gorantiwar.swapnil@gmail.com> wrote:
Hello all,
What is the criteria for PWHT as per ASME B31.3?One is thickness criteria i.e. Carbon steel to be PWHT for thk 20mm and higher or alloy steel 13mm and higherWhat are the other criterias?
--Best Regards,
Swapnil Gorantiwar--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
No comments:
Post a Comment