Dear Farhang,

Check the note A and B below the chemical analysis table.


On Mon, Jan 28, 2013 at 11:57 AM, Farhang <hyperm2m@gmail.com> wrote:

Dear All

I have tested a specimen of A 516 Gr. 70+Normalized (thickness: 10mm) for chemical analyze, impact, tensile & metallographic.

 Tensile & Impact were acceptable, but i have problem in chemical analyze as follow:

 ü Tensile Strength:

Fy: 360 Mpa     UTS: 531  Mpa

 ü Impact Test:

absorbed energy in impact: 150 j    (sub size 7.5*10*55) – it was very good

 ü chemical analyze:

C:0.09/Mn:1.534/Si:0.35/P:0.005/S:0.005/Cr: 0.069/ Ni: 0.046/ Cu: 0.01 /Mo:0.013/ Cu: 0.104/ V:0.055 /W:0.0026 /Ti: 0.027 /AL:0.042/ Sn:0.001/1 Pb:0.0002/ As:0.002/   Sb:0.0023/ Zr:0.0015/ Nb:0.0475/ Ca: 0.0031

 But according to standard ASTM A516(attached) Mn shall be 0.79~1.30 but here   Mn% is over. It was 1.53%  .

 

I need to know the effect of this discrepancy???

Does it important?

Isn't carbon% very low????????

What is high amount of manganese could be causes?????

 

M. Farhang

hyperm2m@gmail.com 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
 
 



--
Thanks & Regards
Biplab Pal
Welding Inspector
E-mail:   biplab.mech@gmail.com
 
Information in this email and any attachments is confidential and intended solely for the use of the individual(s) to whom it is addressed or otherwise directed. Please note that any views or opinions presented in this email are solely those of the author and do not necessarily represent those of the Company. Finally, the recipient should check this email and any attachments for the presence of viruses. Myself accepts no liability for any damage caused by any virus transmitted by this email.
 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
---
You received this message because you are subscribed to the Google Groups "Materials & Welding" group.
To unsubscribe from this group and stop receiving emails from it, send an email to materials-welding+unsubscribe@googlegroups.com.
For more options, visit https://groups.google.com/groups/opt_out.
 
 

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...