Re: [MW:16416] QW407.2 (ASME Sec. IX)

Dear Friend,
Nice to meet you. According to ASME Sec 9, QW 407.2
it is clearly mentioned that the PWHT Soaking temp and time which you
had implemented during procedure qualification has to be essentially
equivalent to your production joint.
Hope it will be clear to you.

Thanks & Best Regards,
Balamurugan.M,
Sr. QA/QC Engg,
L&T Ecc,
UTKAL REFINERY SITE.

On 1/2/13, Tariq Hussain <tariqhussain632@gmail.com> wrote:
> Dear All,
>
> We need little help from you regarding below query for *ASME Sec. IX
> QW-407.2*
>
> * *
>
> Is it intention of *QW-407.2* to have *Production Welds Soak Temperature
> (Vessel Soak temperature)* exactly same as that of done in PQR test Coupon?
>
>
> Thanks in Advance
>
> Tariq Hussain
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
>
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
>
>
>

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm

The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.