[MW:16404] Re: I did preheat in carbon steel by cutting torch instead heating torch. Is it acceptable or not, if not means why?

Can anyone provide proper supporting references to show that preheating by oxy-acetylene gas torch is not correct for normal carbon steel piping with 25mm and above thickness?
Also, SAES-W-011 says clearly the preheating temp for SMAW Butt welds only.Not mentioning about GTAW. So normally to remove moisture reheating is required. After root and hot pass welds, the remaining 26-6mm=20mm which is less than 25mm , and hence no special preheating is required as per my understanding.
can any one suggest any other alternative?

Thanks 
GJRAJU

On Sunday, December 2, 2012 10:03:38 PM UTC+5:30, PK wrote:
Dear Experts,

I did preheat in carbon steel by cutting torch instead heating torch. Is it acceptable or not, if not means why?

Thanks,

Pkm..

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
 
 

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...