Re: [MW:16180] TOFD & Phased Array UT which is Better

The fundamental difference between TOFD and PAUT is as follows:

TOFD
Excellent at detecting and sizing volumetric type indications (i.e. slag, porosity, etc)
Good at detecting and sizing planer indications but is not always good at detecting and worst at sizing close to the surfaces
Sizing of defects with TOFD is problematic due to the nature for which an indication is created by the sound wave.
Can be used where there is a wall thickness transition at the weld.

PAUT or shear wave UT
OK at detecting and sizing volumetric indications.  Typically the sizing is less accurate than TOFD unless the indication is large or a cluster and at a optimum orientation such that the round nature of volumetric indications does not deflection the UT wave.
Excellent at detecting and sizing planer indications such as cracks, lack of fusion, incomplete penetration.
PAUT can also be set to target the surface region to detect indications that TOFD can not see and size.
Typically not possible to use when there is a wall thickness transition at or close to the weld.  The transition needs to be several inches from the weld.

There are advantages and disadvantages to each inspection method.  The method needs to be selected based on what type of indications are expected and targeted in the acceptance criteria.  Usually both TOFD and shear wave UT (PAUT or multiprobe) are used together and both signals are analyzed to determine the type and size of the indications. 

That is a very short summary of the UT methods you asked about.  There are a lot more that needs to be considered and understood when applying either or both method.  That is especially  the case regarding the method of which they are calibrated.

In either case neither is better, they are just different.  One may be better for one situation and the other better in another situation.

Welding Engineer
Houston, Texas


On Fri, Nov 30, 2012 at 1:46 AM, mohd <mohd52100@gmail.com> wrote:
Dear all,

What is different between TOFD& PAUT?
which one is better?

regrds,
mohammed.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
 
 

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
http://www.linkedin.com/groups/MaterialsWelding-122787?home=&gid=122787&trk=anet_ug_hm
 
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
 
 

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...