That is correct. Thickness shall be 10mm.
Note: For face bend specimens, the 5mm removal shall be from the root side. For the root bend specimens, the 5mm removal shall be from the face side.
John A. Henning
Welding & Materials
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of sevak hiren
Sent: Thursday, July 05, 2012 8:15 AM
To: materials-welding@googlegroups.com
Subject: [MW:14771] Thickness of transverse Root Bend & Face Bend test Specimen
Dear Experts,
For a WPS qualification test made on 15 mm thk. SA 516 Gr.60 plate,
What would be the required final thickness for transverse Root Bend & Face Bend test Specimen as per ASME Section IX ?
As per figure QW-462.3(a) it must be 10 mm, am I correct ?
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
______________________________________________________________________
The information in this email is confidential, and is intended solely for the addressee(s). If you are not the intended recipient of this email please let us know by reply and then delete it from your system; you should not copy this message or disclose its contents to anyone. The internet can not guarantee the integrity of this message. HAMON (and its subsidiaries) shall (will) not therefore be liable for the message if modified.
______________________________________________________________________
No comments:
Post a Comment