Dear All.
Thank you for good information.
pls. see attached picture additional info.
pls advice.
thank all.
leonard.
2012/5/8 salman cader <salman96996@gmail.com>
the information i gave you comes from notes i got when i did my cswip
level 2 welding exam .......i never came across welding a hi carbon
steal higher than .4 but this what the notes told me when you welding
a steel of a carbon content higher than .5 so get a second opinion
then....my bad
but when im welding steel of a carbon content of .3 to .4 this is what
id do..... Parts may be readily welded with all process if preheat,
interpass temperature controls, and post heat recommendations are
followed.
Use Low hydrogen Electrodes and appropriate filler wire.
Heat treating after welding may be applied
ue, May 8, 2012 at 4:07 PM, pradeep kumar hormis <pkhormis@gmail.com> wrote:
> Dear Salman
>
> Totally contradictory statements you had given. cann't accept by
> professional welding theory.
>
> On Mon, May 7, 2012 at 5:12 PM, salman cader <salman96996@gmail.com> wrote:
>>
>> Hi you got a Carbon content of .45....use an Austernetic stainless
>> steel consumable because it gives more ductility and and less strength
>> and it will relieve internal stress.but your HAZ zone will still be
>> brittle so you have to do a PWHT(stress relief)temperatures for stress
>> relief range between 550-750 degrees Celsius ..Note 1 hour for every
>> 25mm of thickness so you do the maths and you ll be fine...this is
>> according to procedure
>>
>> Salman
>> Gem Consulting
>>
>>
>> Mon, May 7, 2012 at 7:10 PM, prem nautiyal <prem_nautiyal26@yahoo.com>
>> wrote:
>> > Hi
>> >
>> > Increase the preheat to 150 degrees Celcius min. Interpass temp 250
>> > degrees
>> > celcius max.
>> > Use SMAW E7018-1 electrode.
>> >
>> > I have successfully welded C45 material with E7018-1.
>> >
>> > Regards
>> >
>> > Prem Nautiyal
>> >
>> > From: LeONarD P <metpick@gmail.com>
>> >
>> > To: Materials & Welding <materials-welding@googlegroups.com>
>> > Sent: Saturday, May 5, 2012 10:56 AM
>> >
>> > Subject: [MW:14187] Welding C45 (1045)
>> >
>> > Dear All expert
>> >
>> > Welding C45 (1045) steel (Pivot Boss) to S275JR (main
>> > structure)
>> >
>> > 1045 Pivot Boss is casting part.
>> > S275JR is steel plate
>> >
>> > For a project I need to weld a C45 (1045 steel, 0.45% carbon Thick 100
>> > mm) on a S275JR steel ( Thichness 30 mm.)
>> >
>> > Joint design & condition weld: T-butt joint, double bevel, CJP. Bevel
>> > at S275JR steel.
>> > preheat 110 C
>> > minimum,. interpass temp 220 C max.
>> > by FCAW process.
>> > A5.20 / E71T-1C
>> >
>> >
>> > After weld, the problem is crack appear along on surface casting
>> > part (1045 steel)
>> >
>> > How to solve this problem.
>> >
>> > Thank you very much.
>> > leonardd..
>> >
>> > --
>> > To post to this group, send email to materials-welding@googlegroups.com
>> > To unsubscribe from this group, send email to
>> > materials-welding+unsubscribe@googlegroups.com
>> > For more options, visit this group's bolg at
>> > http://materials-welding.blogspot.com/
>> > The views expressed/exchnaged in this group are members personel views
>> > and
>> > meant for educational purposes only, Users must take their own decisions
>> > w.r.t. applicable code/standard/contract documents.
>> >
>> >
>> > --
>> > To post to this group, send email to materials-welding@googlegroups.com
>> > To unsubscribe from this group, send email to
>> > materials-welding+unsubscribe@googlegroups.com
>> > For more options, visit this group's bolg at
>> > http://materials-welding.blogspot.com/
>> > The views expressed/exchnaged in this group are members personel views
>> > and
>> > meant for educational purposes only, Users must take their own decisions
>> > w.r.t. applicable code/standard/contract documents.
>>
>> --
>> To post to this group, send email to materials-welding@googlegroups.com
>> To unsubscribe from this group, send email to
>> materials-welding+unsubscribe@googlegroups.com
>> For more options, visit this group's bolg at
>> http://materials-welding.blogspot.com/
>> The views expressed/exchnaged in this group are members personel views and
>> meant for educational purposes only, Users must take their own decisions
>> w.r.t. applicable code/standard/contract documents.
>
>
>
>
> --
> Thanks & Regards
>
> PRADEEPKUMAR HORMIS
> Mob: +91-0-9496754791
>
>
>
>
> --
> To post to this group, send email to materials-welding@googlegroups.com
> To unsubscribe from this group, send email to
> materials-welding+unsubscribe@googlegroups.com
> For more options, visit this group's bolg at
> http://materials-welding.blogspot.com/
> The views expressed/exchnaged in this group are members personel views and
> meant for educational purposes only, Users must take their own decisions
> w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
No comments:
Post a Comment