Re: [MW:14199] Welding C45 (1045)

Hi
 
Increase the preheat to 150 degrees Celcius min. Interpass temp 250 degrees celcius max.
Use SMAW E7018-1 electrode.
 
I have successfully welded C45 material with E7018-1.
 
Regards
 
Prem Nautiyal

From: LeONarD P <metpick@gmail.com>
To: Materials & Welding <materials-welding@googlegroups.com>
Sent: Saturday, May 5, 2012 10:56 AM
Subject: [MW:14187] Welding C45 (1045)

Dear All expert

        Welding C45 (1045) steel (Pivot Boss) to S275JR (main
structure)

1045 Pivot Boss is casting part.
S275JR is steel plate

For a project I need to weld a C45 (1045 steel, 0.45% carbon Thick 100
mm) on a S275JR steel ( Thichness 30 mm.)

Joint design & condition weld:  T-butt joint, double bevel, CJP. Bevel
at S275JR steel.
                                                  preheat 110 C
minimum,. interpass temp 220 C max.
                                                  by FCAW process.
A5.20 / E71T-1C


      After weld, the problem is crack appear along on surface casting
part (1045 steel)

How to solve this problem.

Thank you very much.
leonardd..

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.


No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...