Re: [MW:13828] Storage Tanks Steel Plates

Dear Sohaib:

Hi,This is Summer from China, in our steel mills, there is not any secret,please do require for the mill test certificate, if they can not provide that, that means the goods maybe not the exact steel grades you want, be careful about this,

In our steel mills, each batch of goods have their mill test certificates and certificates of origin issued by the local government, please be noted,'

2012/3/4 Fraser Rock <rockweld@live.ca>

Sohaib
I would be very suspect in this situation. There should be nothing secret about the content of steel plate being used.
At the end of the day, you are paying for the ploate, you should know exactly what you are paying to receive.

Doc...Rockweld

Date: Sat, 3 Mar 2012 13:23:50 -0500
Subject: Re: [MW:13816] Storage Tanks Steel Plates
From: jmejialema@gmail.com
To: materials-welding@googlegroups.com

There is no secret they have to show you the real especification by test or by Mill test Report Certificate from the mill. Your paying. Please see API 650 Standard.
Regards
jml from Colombia

2012/3/3 SOHAIB GHNAIMAT <sohaib_cegco@yahoo.com>

Gents,

We have an issue with the steel plate manufacturer that he is getting the Raw material in the form of steel slabs from other country, and he is doing the Pre-heating and rolling....etc for the Steel slabs to get the final required steel plates.

Do we require having a mill test certificate for the steel slabs, or is enough to have it for the final steel plates.

The supplier is telling that for the steel slabs all information is secret! Do we need to have the manufacturing process, inspection & test plan for the steel slabs.

He has issued the Inspection & test plan for the processing of steel slabs to final steel plates.

Please advice.

Sohaib

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Summer Song

Sales Maneger

HENAN BEBON INTERNATIONAL CO., LTD

T: +86-371-86151527 F: +86-371-86011881

Mobile: +86-13783594495

E-mail: bebonsummer@bebonchina.com

Web: www.bebonchina.com

www.steel-plate-sheet.com

www.shipbuilding-steel.com

SKYPE: bebonsummer

MSN: bebonsummer@hotmail.com

Lowest Price--Fast Delivery --Best Quality

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog