[MW:13575] RE: 13563] Interpret IX-04-15

Hi

 

 

The post weld heat treatment can be any of heat treatment type like normalizing & tempering, annealing, solution annealing, stress relieving (each having different temperature limits) etc depends upon the type of steel and code of construction. And similarly the time ranges also.

 

So, the Code restricts that the user to use the same heat treatment and time as encountered in the production joint.

That’s why it is restricted to use the PQR at least meeting the 80% of time(s) at temperature(s) as encountered on the production joint.

BR

M.Vijayan

 

From: Somkiat Patcharanaruemon [mailto:soiy7777777@gmail.com]
Sent: Thursday, January 26, 2012 5:37 AM
To: Vijayan Munuswamy
Cc: materials-welding@googlegroups.com
Subject: Re: 13563] Interpret IX-04-15

 

Dear Vijayan

Thanks you very much for your advice but I still confuse because in QW 407.2 state that  "A change in temperature and time range" and this WPS change only in time range but temperature still the same so this clause shouldn't be essential variable otherwise  why the code shouldn't state"A change in temperature or time range" instead of "A change in temperature and time range" please advice.

BRG

Solomon

2012/1/25 vijayan <vijayan.m@madinagulf.com>

Hi

Because the wps is not written as per the QW.407.2. it means the WPS can
support only up to 108 minutes (not 3.5 Hours)

BR
M.Vijayan


-----Original Message-----
From: materials-welding@googlegroups.com
[mailto:materials-welding@googlegroups.com] On Behalf Of solomon
Sent: Wednesday, January 25, 2012 4:45 AM
To: Materials & Welding
Subject: [MW:13563] Interpret IX-04-15

Dear Expert
.
According to interpretation below could you please explain why the answer is
"No". In my understanding WPS has change only time range but doesn't change
in the temperature(logic "and" mean change both time and temperature).

In SEC IX  QW-407.2 state that "A change in the postweld heat treatment (see
QW-407.1) temperature and time range"

Interpretation: IX-04-15
Subject: QW-403.7, Base Metal Thickness Qualification and QW-407.2, PWHT
Temperature and Time Range Date Issued: December 22, 2004
File: BC04-1595
Question (1): Will a procedure qualification test coupon on 1.5 in.
thick P-No. I, Gr. 2 material and
postweld heat-treated at I,lOO°F for 1.5 hr with supplementary essential
variable requirements met, support a WPS with supplementary essential
variable requirements for production welding on 8 in. thick P-No. 1, Gr. 2
material that is PWHT at l,lOO°F for 3.5 hr?
Reply (1): No

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to
materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at
http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and
meant for educational purposes only, Users must take their own decisions
w.r.t. applicable code/standard/contract documents.



This communication and any files transmitted with it are confidential and may also be privileged. It is for the exclusive use of the intended recipient(s). If you are not the intended recipient or the person responsible for delivering it to the intended recipient(s), please note that any form of distribution, copying or use of this communication or information contained in it is strictly prohibited and may be unlawful. If you have received this communication in error please return it to the sender, and delete the material from any computer. We reserve the right to monitor email communications through normal internal and external networks. We believe but not warrant that the email and the attachments are virus free. The statement and opinions expressed in this communication are those of the writer and do not necessarily represent those of Madina Group, whose registered office address is

P.O. Box 20459, Doha, Qatar.
Tel. +974 44600818
Fax. +974 44603143

 



This communication and any files transmitted with it are confidential and may also be privileged. It is for the exclusive use of the intended recipient(s). If you are not the intended recipient or the person responsible for delivering it to the intended recipient(s), please note that any form of distribution, copying or use of this communication or information contained in it is strictly prohibited and may be unlawful. If you have received this communication in error please return it to the sender, and delete the material from any computer. We reserve the right to monitor email communications through normal internal and external networks. We believe but not warrant that the email and the attachments are virus free. The statement and opinions expressed in this communication are those of the writer and do not necessarily represent those of Madina Group, whose registered office address is

P.O. Box 20459, Doha, Qatar.
Tel. +974 44600818
Fax. +974 44603143