Re: [MW:12692] CLAD MATERIALS -WELDING

I think the welding to be done in foll.manner.    first of all grind/flush the clad material up to the surface of the 5L grade pipe...prepare the ends of the 5L pipes to be welded together,root,fill by suitable electrode up to the basepipe thickness....flush the uper surface of the welding.....then prepare the ends of the clad material and then overlay welding by suitable electrode......... 

On Oct 16, 2011 3:50 PM, "Sundaram Elumalai" <Elumalai.Sundaram@starfab.com.sa> wrote:

Hi experts,

 

We have the following Clad Pipe and we are preparing WPS /PQR to weld this SPOOL. As I know we need to use ERNiCrMo3 / E NiCrMo 3 ( if GTAW+SMAW) to Complete weld. But if any one is having experience with this, please advice whether we will go with

 

GTAW -  ER NiCrMo3  ( First four Passes- R/H/F1/F2)

SMAW – E7018-1  ( Balance Filling /Capping).

 

We have Pitting corrosion test as per ASTM G48 at 50 degree.

 

Pipe

NPS:10-Thk:45mm-PIPE-API 5L GR.X65 PSL2 - SMLS -GA-E-61036

BW

3mm Inconel Cladded

Pipe

NPS:12-Thk:15.88mm-PIPE-API 5L GR.X65 PSL2 - SMLS -GA-E-61036

BW

3mm Inconel Cladded

Pipe

NPS:12-Thk:45.5mm-PIPE-API 5L GR.X65 PSL2 - SMLS -GA-E-61036

BW

3mm Inconel Cladded

Pipe

NPS:12-Thk:53.5mm-PIPE-API 5L GR.X65 PSL2 - SMLS -GA-E-61036

BW

3mm Inconel Cladded

 

 

 

With Kind Regards,

 

S.Elumalai.

******************************************************************************************
CONFIDENTIALITY NOTICE
This e-mail and any attachment are confidential and may be privileged or otherwise protected from disclosure. It is solely intended for the person(s) named above. If you are not the intended recipient, any reading, use, disclosure, copying or distribution of all or parts of this e-mail or associated attachments is strictly prohibited. If you are not an intended recipient, please notify the sender immediately by replying to this message or by telephone and delete this e-mail and any attachments permanently from your system.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...