Wednesday, October 26, 2011

[MW:12774] RE: PWHT in TP 321

By any chance does your project spec calls for "Stabilization anneal". It's
a post fabrication anneal(850-900 deg C)applied for stabilized stainless
steels to improve the post fabrication corrosion resistance.

If you could provided more details, I could write to more about the pros and
cons of this method.

Thanks.

Pradip Goswami,P.Eng.IWE
Welding & Metallurgical Specialist & Consultant
Ontario,Canada.
Email-pgoswami@sympatico.ca,
pgoswami@quickclic.net

-----Original Message-----
From: pradip kumar sil [mailto:pradipsil@gmail.com]
Sent: Wednesday, October 26, 2011 2:17 AM
To: materials-welding@googlegroups.com
Cc: pgoswami
Subject: PWHT in TP 321

Dear Everybody,
First of all Wise you a happy diwali to you & your family.
In my project specification says ASTM A 312 TP 321 has PWHT. My question is
why we will do TP 321 needs to do PWHT because this material have high Cr/Ni
as well as Ti.
Regards
Pradip


--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...