Re: [MW:11600] RE: 11595] E7018-A1 Electrod


Dear Pgoswami,
 
As per SEC IX- 2007; QW/QB-422  SA 210 A-1 comes under Pno:1 Gr 1 and I had referred
SEC II part A and found that there is no Molybenum in it. Could you please verify it?
 
Regards
Ilangkumaran 
--- On Wed, 7/6/11, pgoswami <pgoswami@quickclic.net> wrote:

From: pgoswami <pgoswami@quickclic.net>
Subject: [MW:11596] RE: 11595] E7018-A1 Electrod
To: materials-welding@googlegroups.com
Date: Wednesday, July 6, 2011, 5:39 AM

Hi Zakaria,
 
E-7018-A1 is C-0.5 Mo electrode while E-7018 is just C-Mn electrode. The base metals are  A 210Gr A1(C-0.5Mo, Sec IX-P3 material) and P11(1 or 1.25 Cr- 0.5 Mo), P4) material.
 
So for room temperature tensile, high temperature Creep properties, E-7018-A1 would be the minimum requirement as it meets all the room temperature tensile strength and elevated temperature creep strength of the leaner alloys (P3).
 
See Sec-II, Pt-C, SFA 5.5, Table-2 (for C-Mo electrodes, E-7018-A1) and SFA 5.1, Table-7 for C-Mn(E-7018) electrodes.
 
You should not replace E-7018-A1 with E-7018. This would endanger the weld and make it prone to failure in service.
 
Thanks.
 
Pradip Goswami,P.Eng.IWE
Welding & Metallurgical Specialist & Consultant
Ontario,Canada.
Email-pgoswami@sympatico.ca,
 


From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Zakaria ghrab
Sent: Tuesday, July 05, 2011 11:12 AM
To: materials-welding@googlegroups.com
Subject: [MW:11595] E7018-A1 Electrod

Hi All,

  In our boiler project we have to weld socket tube A210 Gr A1,  38 mm diameter , 4 mm thick  to collector P11 material thick , according client WPS we have to weld by E7015-A1.

What's the difference between EXXXX and EXXXX-A1
May E7018 substitue E7015-A1 ?

Kind regards

--
زكرياء غراب
GHRAB Zakaria
مسؤول عن الجودة
QA/QC SENAD
مشروع المحطة الحرارية ـ الوحدة الرابعة
المحمدية ـ المغرب

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

Re: [MW:34832] Inquiry about Single Bevel with Back Grinding

Dear Uday, As per your question that one is called with backing only,Simple both side you are welding it is backing with strip or without st...