RE: [MW:10778] Impact testing temp. for EN19 steel

Manpeet,
 
Izod is for plastics, charpy V notch ductility tesying is common on steels.
 

Kind regards

Met vriendelijke groeten,
Namens Kiwa N.V.

Ing. L. Lossie
IWE / I&K III
Senior inspecteur

Fax: (+31) 070-414 4420
Mobiel: (+31) 06-51615714
Email: bert.lossie@kiwa.nl

-----Original Message-----
From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Magdum.Manmmet@akersolutions.com
Sent: 21 April 2011 05:58
To: materials-welding@googlegroups.com
Subject: RE: [MW:10767] Impact testing temp. for EN19 steel

Hello !

 

Please can someone answer my general query>

 

Why only Charpy V Notch Testing is mostly used for Impact Testing & why Izod is not  popular.

 

Please give detailed information to understand process thoroughly.

 

Waiting for replies!

 

Regards,
Manmeet Magdum
Document Quality Control Drilling Riser Systems
QS Supply Chain.
AkerSolutions

( (Tel ) +91-20-66918751

Ë (Mobile) +91 9762446730
* (Email) Magdum.Manmmet@akersolutions.com

Aker Powergas Subsea   Pvt Ltd
BlueRidge , IT-2, Flagship Infrastructure Pvt Ltd, Ist Floor, Hinjewadi, Pune 411045, India

Registered in India ; CIN;U74990MH2010PTC210736

 


From: materials-welding@googlegroups.com [mailto:materials-welding@googlegroups.com] On Behalf Of Kathalingam Babu
Sent: Thursday, April 21, 2011 5:47 AM
To: materials-welding@googlegroups.com
Subject: Re: [MW:10765] Impact testing temp. for EN19 steel

 

Hi

 

Izod will be done at Room temp.,  Unless  otherwise specifically mentioned by spec.

 

Thanks & Regards,

 

K. Babu

----- Original Message -----

Sent: Wednesday, April 20, 2011 11:21 PM

Subject: [MW:10758] Impact testing temp. for EN19 steel

 

Dear Friends

I wanted to use EN 19 plate in one of my present project, wherein the application demands severe impact loads at room temperature.

I had browsed through the properties of EN 19 plate in various literatures wherein the Izod test values are mentioned @ 55J.

However the Izod testing temperature is not mentioned.

Can anyone help me out or guide me where to refer, so that i can know the Izod testing temperature of this EN 19 steel.

Secondly i would also like to know which of the two will have more toughness and why - EN 19 casting OR EN19 plate ?
The reason being the final component will have to be casted due geometrical complications.


Regards

Prem Nautiyal


PREM S NAUTIYAL
CELL : 9769316004

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.


This e-mail and any attachment are confidential and may be privileged or otherwise protected from disclosure. It is solely intended for the person(s) named above. If you are not the intended recipient, any reading, use, disclosure, copying or distribution of all or parts of this e-mail or associated attachments is strictly prohibited. If you are not an intended recipient, please notify the sender immediately by replying to this message or by telephone and delete this e-mail and any attachments permanently from your system.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

No comments:

[MW:34820] RE: 34813] Clarification in Rate of heating and cooling.

Hello,   Please see the response below.   Regards.   P. Goswami, P. Eng, IWE.   From: materials-welding@googlegroups.com <materials-weld...