Re: [MW:10715] Re: WPS Qualification / Pressure Vessel / ASME Sec VIII, Div 1

Dear Raj,

Thanks for the information, but still the query is not answered.

There is no Impact Test requirement for our Vessel.

Now can you please guide, whether i can prepare a WPS with an ASTM Material.

Thanks & Regards

Vino-Doha, Qatar

________________________________________________________________________

On Mon, Apr 18, 2011 at 7:34 AM, Raj <raj.inspection@gmail.com> wrote:

Hi,

Please refer UG-84(h)(2) of ASME Sec VIII Div.1'Ed'2010.

If impact testing is required in weld & HAZ when required by UCS-67,
the following shall apply.

For vessels constructed to the rules of part UCS, the test plate
material shall sitisfy all of the following requirements relative to
the material to be used in production.

(a) be of the same P-Number and Group Number;
(b) be in the same heat treated condition; and
(c) meet the minimum notch toughness requirements of UG-84(c)
(4) .......................

Means, one way or other, If you are using LTCS material for production
and requires notch touchness of weld and HAZ then the base material
used for Procedure shall be of same P No..(You can use ASTM A333 Gr.
6(P1G1) to ASTM A350LF2(P1G2) procedure) but you can not use ASTM A106
Gr.B even though it is P1G1 since it "is not the same heat treated
condition" as that of A333 gr.6.

Hope this will clarify!

Cheers!

Raj

On Apr 17, 4:37 pm, Vino Varghese <vinopvargh...@gmail.com> wrote:
> Dear All,
>
> Design Code: ASME Sec VIII, Div 1
> U-Stamp Pressure Vessel
>
> Reference Code : ASME Sec IX, Edition 2007, Add 09
> Material of Construction: SA 516 Gr 70N(30mm thk)
> PQR Material : *1. Pipe* - ASME SA 333 and *2. Flange* : ASTM A350 LF2
>
> *Query:*
> *Is it mandatory that Qualification has to be done only with a ASME
> Material? *
> *If ASTM Material is used for qualification, then WPS will be qualified only
> for that particualr Material and cannot be Qualified as P1 Material. Please
> provide all reference from Code for justification*.
>
> Hope to see that i was able to communicate properly with regard to raised
> query.
>
> Expecting as usual response from all sides.
>
> Thanks & Regards
> Vino-Doha

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

--
To post to this group, send email to materials-welding@googlegroups.com
To unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.com
For more options, visit this group's bolg at http://materials-welding.blogspot.com/
The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.

Re: [MW:34105] SA266 GR4N 4 Cycle SPWHT

Hi, You are correct, Minimum refers to the one cycle for which this part will expose until final work shop PWHT. hence mill test certificate shall include this. Max. SPWHT, refers to additional cycles of heat treatment that are reserved for future repairs during equipment lifetime. Again, these simulated no. Of cycles shall be specified in MTC. The idea is we need to make sure that steel mechanical properties are not compromised upon exposure to multiple repairs (i e 4 cycles in your case). One could say, if steel is subjected to 4 cycles and is ok, then it should by defacto be good for one cycle, yet, this is wrong assumption cause mechanical problems and microstructure of materials varies accordingly based on no. Of cycles for which material will expose. This is apparent in alloy steel and especially for impact test values as an example. In your case, this forged CS with properties before PWHT can be understood to be " as forged" condition (i.e. Wit...

Materails FAQs

Q: What are equivalents for standard Q 235 B (and Q 235 A) for U-channels? (asked by: boris.vielhaber@vait.com) A: DIN Nr. = 2393 T.2, 2394 T.2, EN 10025 W. Nr. DIN 17007 = 1.0038 Design DIN 17006 = RSt 37-2, S235JRG2 (Fe 360 B) Q: What is St DIN 2391 BK material? (asked by: dmcandrews@automaticstamp.com) A: Precision steel tubes, cold-finished/hard. Q: What is C.D.W. Boiler Tube? (asked by: montydude123@yahoo.com) A: Cold Drawn Welded Boiler Tube. Q: WHAT IS W.Nr. 1.4301? PLS TELL US IN EASY LANGUAGUE (asked...

Heat tint (temper) colours on stainless steel surfaces heated in air // Heat tint

Introduction The colour formed when stainless steel is heated, either in a furnace application or in the heat affected zone of welds, is dependent on several factors that are related to the oxidation resistance of the steel. The heat tint or temper colour formed is caused by the progressive thickening of the surface oxide layer and so, as temperature is increased, the colours change. Oxidation resistance of stainless steels However, there are several factors that affect the degree of colour change and so there is no a single table of colour and temperature that represents all cases. The colours formed can only be used as an indication of the temperature to which the steel has been heated. Factors affecting the heat tint colours formed Steel composition The chromium content is the most important single factor affecting oxidation resistance. The higher the chromium, the more heat resistant the steel and so the development of the heat tint colou...

Materials & Welding

Search This Blog