910 drg.C it's possible to have Witmansttaten structures=DANDEROUS
From: james gerald <gerry_tup@yahoo.com>
To: materials-welding@googlegroups.com
Sent: Monday, March 7, 2011 1:03 PM
Subject: Re: [MW:10199] normalizing temperature range for CS materials
-- To post to this group, send email to materials-welding@googlegroups.comTo unsubscribe from this group, send email to materials-welding+unsubscribe@googlegroups.comFor more options, visit this group's bolg at http://materials-welding.blogspot.com/The views expressed/exchnaged in this group are members personel views and meant for educational purposes only, Users must take their own decisions w.r.t. applicable code/standard/contract documents.
To: materials-welding@googlegroups.com
Sent: Monday, March 7, 2011 1:03 PM
Subject: Re: [MW:10199] normalizing temperature range for CS materials
Normally it is 910degC. It depends on the chemical composition and you can plot it in Fe-C equilibrium diagram above AC3 temperature point. J.GERALD JAYAKUMAR 00919344954677 --- On Mon, 3/7/11, iacob catalin <cataliniacob2000@yahoo.com> wrote:
|